Title: dc- and ac-magnetic field-induced strain effects in ferromagnetic shape memory composites of Ni–Mn–Ga single crystal and polyurethane polymer
Authors: Zeng, Min
Or, Derek Siu-wing
Chan, Helen L. W.
Subjects: Ferromagnetic materials
Gallium alloys
Internal stresses
Laminates
Magnetic multilayers
Magnetomechanical effects
Manganese alloys
Nickel alloys
Polymers
Sandwich structures
Shape memory effects
shrinkage
Issue Date: 1-May-2010
Publisher: American Institute of Physics
Source: Journal of applied physics, 1 May 2010, v. 107, no. 9, 09A942, p. 1-3.
Abstract: Ferromagnetic shape memory composites of multilayer and sandwich types were fabricated by laminating Ni–Mn–Ga single-crystal plates with polyurethane (PU) polymer plates. The dc- and ac-magnetic field-induced strains (MFISs) in the composites were measured as functions of both magnetic field and mechanical load, and the results were compared with those of the single crystal. It was found that the load-free dc-MFISs were 5.6%, 1.5%, and 0.8%, while the load-free ac-MFISs were 0.3%, 0.8%, and 0.5% in the single crystal, multilayer composite, and sandwich composite, respectively. The relatively smaller load-free dc-MFISs and larger load-free ac-MFISs in the composites than the single crystal originated from the stress bias of the Ni–Mn–Ga plates by the PU plates in the composites. The dc-MFISs of all samples and the ac-MFISs of the composites decreased with the increase in mechanical load amplitude, while the ac-MFIS of the single crystal peaked at 1.6 MPa load.
Rights: © 2010 American Institute of Physics. This article may be downloaded for personal use only. Any other use requires prior permission of the author and the American Institute of Physics. The following article appeared in M. Zeng, S.W. Or & H.L.W. Chan, J. Appl. Phys. 107, 09A942 (2010) and may be found at http://link.aip.org/link/?jap/107/09A942
Type: Journal/Magazine Article
URI: http://hdl.handle.net/10397/2490
DOI: 10.1063/1.3357408
ISSN: 0021-8979 (print)
1089-7550 (online)
Appears in Collections:AP Journal/Magazine Articles
EE Journal/Magazine Articles

Files in This Item:
File Description SizeFormat 
JApplPhys_107_09A942.pdf294.85 kBAdobe PDFView/Open


All items in the PolyU Institutional Repository are protected by copyright, with all rights reserved, unless otherwise indicated. No item in the PolyU IR may be reproduced for commercial or resale purposes.